No. of cable |
/ |
24~30 |
32~60 |
62~72 |
96 |
||
Design (StrengthMember+Tube&Filler) |
1+5 |
1+5 |
1+6 |
1+8 |
|||
Fiber type |
/ |
G.652D |
|||||
Central Strength Member |
Material |
mm |
FRP |
||||
Diameter (±0.05mm) |
1.5 |
1.5 |
2.1 |
2.1 |
|||
Loose Tube |
Material |
mm |
PBT |
||||
Diameter (±0.05mm) |
1.8 |
2.1 |
2.1 |
2.1 |
|||
Thickness (±0.03mm) |
0.32 |
0.35 |
0.35 |
0.35 |
|||
MAX.NO./per |
6 |
12 |
12 |
12 |
|||
Water Blocking Layer |
Material |
/ |
Flooding Compound |
||||
Inner Sheath |
Material |
mm |
MDPE |
||||
Thickness |
0.9(nominal) |
||||||
colour |
black. |
||||||
Additional Strength Member |
Material |
/ |
Aramid Yarn |
||||
Outer Sheath |
Material |
mm |
MDPE |
||||
Thickness |
1.8(nominal) |
||||||
colour |
black. |
||||||
Cable Diameter(±0.2mm) |
mm |
11.1 |
11.7 |
12.3 |
14.1 |
||
Cable Wetght(±10.0kg/km) |
kg/km |
100 |
111 |
122 |
135 |
||
Attenuation coefficient |
1310nm |
dB/km |
≤0.35 |
||||
1550nm |
≤0.21 |
||||||
Cable breaking strength(RTS) |
kn |
≥12.0 |
|||||
Working Tension (MAT) |
Kn |
≥5.0 |
|||||
Wind velocity |
m/s |
30 |
|||||
Icing |
mm |
5 |
|||||
Span |
M |
200 |
|||||
Crush Resistance |
Short Term |
N/100mm |
≥2200 |
||||
Long Term |
≥1100 |
||||||
Min. bending radius |
Without Tension |
mm |
10.0×Cable-φ |
||||
Under Maximum Tension |
20.0×Cable-φ |
||||||
Temperature range (℃) |
Installation |
℃ |
-20~+60 |
||||
Transport&Storage |
-40~+70 |
||||||
Operation |
-40~+70 |